Paste PVC resin (micro-suspension process)

 

I. Product property:

PVC resin is a PVC homopolymer and can be mixed with plasticizer and other additives to form PVC paste. The past PVC resin is applicable to process technologies including coating, dipping, spray coating, foaming and rotational forming.

II. Quality index: Q/SHG 1—2011

Item

Designation

PSH-10

PSH-30

PSM-31

PSL-31

Resin

Appearance

White ultrafine powder

Degree of polymerization

1580-1780

1630-1830

1230-1430

800-1080

Volatile matter percent ≤

0.50

Bulk density g/cm3

0.2-0.45

Sieve residue mg/kg≤ (0.15mm sieve pore diameter)

10.0

Residual vinyl chloride monomer mg/kg≤

5.0

Mixture

Type B viscosity (30℃) mPa.s

Resin: DOP =100:65

1000-2500

1500-6500

1500-6500

1500-6500

Scratch granularity μm≤

100

III. Application:

PSH-10: non-foaming artificial leather bottom layer, artificial leather and floor leather surface layer, canvas, dip forming products (gloves, shoes, etc.), rotational forming products (bobble heads, toys), slush molding products, scrapers, bottle cap mats and more.

PSH-30: PVC emulsion gloves, artificial leather surface layer and more.

PSL-31: foaming wallpaper, floor leather, artificial leather, rotational forming products, etc.

IV. Packaging:

The product is packaged with a paper bag (internally lined with plastic woven net) with cuff. The net weight of each bag is 20kg. The types are differentiated as per the idnetification color on the bag: PSH-10 yellow, PSH-30 blue, PSM-31 red and PSL-31 green.

V. Storage and transportation:

Protect it from rain, snow, moisture, insulation, bag throwing and other mechanical damage.

Note: Our company can provide customized technical indexes products.

Contact:

South China market: 024-25553106, 25553064

North China market: 024-25553118, 25553117

Media Inquiry
Tel:024-23862817
 
Contact Us | Site Map | Legal | Links | RSS
Shenyang Chemical Co Ltd's all rights reserved.Without written authorization from China
National BlueStar (Group) Co.Ltd. such content shall not be republished or used in any form.